融点 | 1840 °C | 沸点 | 2900 °C | 比重(密度) | 4.26 g/mL at 25 °C(lit.) | 屈折率 | 2.61 | 闪点 | 2500-3000°C | 貯蔵温度 | Store at +5°C to +30°C. | 溶解性 | Practically insoluble in water. It does not dissolve in dilute mineral acids but dissolves slowly in hot concentrated sulfuric acid. | 外見 | powder | 比重 | 4.26 | 色 | White to slightly yellow | PH | 7-8 (100g/l, H2O, 20℃)(slurry) | 臭い (Odor) | at 100.00?%. odorless | 水溶解度 | insoluble | Crystal Structure | Orthorhombic, Pcab | Merck | 14,9472 | 暴露限界値 | ACGIH: TWA 10 mg/m3 OSHA: TWA 15 mg/m3 NIOSH: IDLH 5000 mg/m3; TWA 2.4 mg/m3; TWA 0.3 mg/m3 | CAS データベース | 13463-67-7(CAS DataBase Reference) | IARC | 2B (Vol. 47, 93) 2010 | NISTの化学物質情報 | Titanium dioxide(13463-67-7) | EPAの化学物質情報 | Titanium dioxide (13463-67-7) |
| 二酸化チタン Usage And Synthesis |
定義 | 本品は、チタンの酸化物であり、次の化学式で表される。 | 解説 | 二酸化チタンは,チタンの酸化物の一、酸化チタン(Ⅳ)。チタンの酸化物の中で最も安定で、天然には金紅石きんこうせき(正方晶系)、鋭錐石えいすいせき(正方晶系)、板チタン石(斜方晶系)などの鉱物として産する。酸化チタン。チタニア。チタンと酸素の化合物。酸化チタン(Ⅳ)とも、チタニアtitaniaともよばれる。チタン(Ⅳ)塩水溶液の加水分解で沈殿した水酸化チタン(Ⅳ)を強熱すると得られる。天然にはルチル(金紅石、正方晶系)、鋭錐石(えいすいせき)、板チタン石(斜方晶系)のそれぞれ結晶構造の異なる鉱物として産出する。アルカリと硫酸には溶けるが、それ以外の酸と水には溶けない。藤嶋昭(1942― )と本多健一(1925―2011)による二酸化チタン電極光触媒効果(本多・藤嶋効果)の発見(1968)から、光触媒としての開発研究が活発に続けられている。[岩本振武] | 解説 | TiO2(79.87).3種類の結晶形が存在し,天然にも3種類の変態,ルチル(rutil),鋭すい石(anatase),板チタン石(brookite)として産出するが,ルチルがもっとも普通である.いずれも融点1640 ℃.3000 ℃ 以上で分解する.人工的には,四価のチタン塩水溶液の加水分解により得られた含水酸化物を強熱するか,四塩化チタンを高温気体状態で酸素と反応させると得られる.含水酸化物を焼くことにより得られるものは,通常,鋭すい石型であるが,高温で焼くとルチル型となる.四塩化チタンと酸素との反応で得られるものはルチル型である.密度4.26 g cm-3.二酸化チタンはアルカリ,硫酸に可溶,冷水,熱水,その他の酸に不溶.微粉末状の二酸化チタンはチタン白の名の顔料として,塗料,ゴム,繊維,樹脂,磁器,研磨剤,金属チタンの製造原料,化粧品,紫外線防止剤,光触媒,光電極などに広く利用されており,天然産,あるいは人工的に粉末状の二酸化チタンを溶融してつくった塊状の二酸化チタンは,チタニアという名で宝石として使用されている.[CAS 13463-67-7:TiO2(ルチル)][CAS 1317-70-0:TiO2(アナターゼ)] 森北出版「化学辞典(第2版) | 用途 | 塗料?印刷インキ?インクジェットインキ?プラスチックの着色顔料,化粧品?シリコーンゴム?プラスチック繊維?磁気テープ?トナー?セラミックスなどの配合原料 (NITE CHRIP) | 化粧品の成分用途 | 不透明化剤、褪色防止剤、着色剤、紫外線吸収剤.散乱剤 | 効能 | 皮膚保護薬 | 主な用途/役割 | ポリウレタン系接着剤に使用される。 | 説明 | Titanium dioxide, TiO2, is a white powder and has the greatest hiding power of all white pigments. It is noncombustible; however, it is a powder and, when suspended in air, may cause a dust explosion if an ignition source is present. It is not listed in the DOT Hazardous Materials Table, and the DOT does not consider it hazardous in transportation. The primary uses are as a white pigment in paints, paper, rubber, and plastics; in cosmetics; in welding rods; and in radioactive decontamination of the skin. | 化学的特性 | White, amorphous, odorless, and tasteless nonhygroscopic powder.
Although the average particle size of titanium dioxide powder is less
than 1 mm, commercial titanium dioxide generally occurs as
aggregated particles of approximately 100 mm diameter.
Titanium dioxide may occur in several different crystalline
forms: rutile; anatase; and brookite. Of these, rutile and anatase are
the only forms of commercial importance. Rutile is the more
thermodynamically stable crystalline form, but anatase is the form
most commonly used in pharmaceutical applications. | 化学的特性 | The naturally occurring dioxide exists in three crystal forms: anatase, rutile and brookite. While rutile, the most common form, has an octahedral structure. Anatase and brookite have very distorted octahedra of oxygen atoms surrounding each titanium atom. In such distorted octahedral structures, two oxygen atoms are relatively closer to titanium than the other four oxygen atoms. Anatase is more stable than the rutile form by about 8 to 12 kJ/mol (Cotton, F.A., Wilkinson, G., Murillo, C.A and M Bochmann. 1999. Advanced Inorganic Chemistry, 6th ed, p. 697, New York: John Wiley & Sons) Other physical properties are: density 4.23g/cm3; Mohs hardness 5.8 g/cm3 ( anatase and brookite) and 6.2 g/cm3 ( rutile); index of refraction 2.488 (anatase), 2.583 (brookite) and 2.609 (rutile); melts at 1,843°C; insoluble in water and dilute acids; soluble in concentrated acids.
| 化学的特性 | Ttitanium dioxide is an odorless white powder. | 物理的性質 | The naturally occurring dioxide exists in three crystal forms: anatase, rutile and brookite. While rutile, the most common form, has an octahedral structure. Anatase and brookite have very distorted octahedra of oxygen atoms surrounding each titanium atom. In such distorted octahedral structures, two oxygen atoms are relatively closer to titanium than the other four oxygen atoms. Anatase is more stable than the rutile form by about 8 to 12 kJ/mol (Cotton, F.A., Wilkinson, G., Murillo, C.A and M Bochmann. 1999. Advanced Inorganic Chemistry, 6th ed, p. 697, New York: John Wiley & Sons) Other physical properties are: density 4.23g/cm3; Mohs hardness 5.8 g/cm3 ( anatase and brookite) and 6.2 g/cm3 ( rutile); index of refraction 2.488 (anatase), 2.583 (brookite) and 2.609 (rutile); melts at 1,843°C; insoluble in water and dilute acids; soluble in concentrated acids. | 使用 | Titanium Dioxide is a white pigment that disperses in liquids and
possesses great opacifying power. the crystalline modifications of
titanium dioxide are rutile and anatase, of which only anatase finds
use as a color additive. | 使用 | titanium dioxide (TiO2) is one of the 21 FDA-approved sunscreen chemicals with an approved usage level of 2 to 25 percent. When applied, titanium dioxide remains on the skin’s surface, scattering uV light. It is often used in conjunction with other sunscreen chemicals to boost the product’s SPF value, thus reducing the risk of irritation or allergies attributed to excessive usage of chemical sunscreens. Its incorporation into sunscreen formulations, makeup bases, and daytime moisturizers depends on the particular size of titanium dioxide employed. The smaller the particle size, the more unobtrusive Tio2’s application. Large particles, on the other hand, leave a whitish wash or look on the skin. Some companies list “micro” or “ultra” when referring to the size of the titanium dioxide particle. According to some sources, titanium dioxide could be the ideal uVA/uVB protection component given its chemical, cosmetic, and physical characteristics. Titanium dioxide is also used to provide a white color to cosmetic preparations. | 使用 | Titanium dioxide is an extreme white and bright compound with high index of refraction. In paints it is a white pigment and an opacifying agent.It is in house paints, water paints, lacquers, enamels, paper filling and coating, rubber, plastics, printing ink, synthetic fabrics, floor coverings, and shoe whiteners. Also, it is used in colorants for ceramics and coatings for welding rods. A rutile form of the dioxide is used in synthetic gem stones.
| 使用 | Airfloated ilmenite is used for titanium pigment manufacture. Rutile sand is suitable for welding-rod-coating materials, as ceramic colorant, as source of titanium metal. As color in the food industry. Anatase titanium dioxide is used for welding-rod-coatings, acid resistant vitreous enamels, in specification paints, exterior white house paints, acetate rayon, white interior air-dry and baked enamels and lacquers, inks and plastics, for paper filling and coating, in water paints, tanners' leather finishes, shoe whiteners, and ceramics. High opacity and tinting values are claimed for rutile-like pigments. | 主な応用 |
Industry
Application
Role/benefit
Pigment
Optical coating for dielectric mirrors and gemstones
Brightness and very high refractive index
Paper coating
Helps to make paper whiter, brighter and more opaque
Plastics, adhesives and rubber
Helps minimize the brittleness, fading and cracking that can occur as a result of light exposure
Food Contact materials and ingredients
Prevents premature degradation and enhance the longevity of the product
Paints
Gives paint its high gloss and rich depth of color
Ceramic glazes
Acts as an opacifier and seeds crystal formation
Cosmetic
Sunscreens
Active ingredients/high refractive index and strong UV light absorbing capabilities
Daily cosmetics or make-up materials
Additive/aids in hiding blemishes and brightening the skin
Toothpastes
Additive/helps to whiten tooth
Catalyst
Dye-sensitized solar cell
Can produce electricity in nanoparticle form
Hydrolysis reaction
Catalyzes the photo decomposition of water into hydrogen and oxygen
Automotive, power stations, etc.
Helps to removes harmful exhaust gas emissions, such as nitrous oxides, volatile organic compounds, etc.
Detoxification or remediation of wastewater
Photocatalytically mineralizes pollutants (to convert into CO2 and H2O) in waste water
Photocatalytic antimicrobial coating
Photocatalytic destruction of organic matter
Others
Oxygen sensor
The electrical resistivity of TiO2 can be correlated to the oxygen content of the atmosphere
Anti-fogging coatings and self-cleaning windows
Under exposure to UV light, TiO2 becomes increasingly hydrophilic
Coated ceramic tile
Disinfectant and self-cleaning qualities
Treatment of the air in fruit, vegetable and cut flower storage areas
Removes ethylene gas to prevent spoilage and prevents internal combustion
Memristor
Can be employed for solar energy conversion
Mixed conductor
Significant ionic and electronic conduction
| 製造方法 | Titanium dioxide is mined from natural deposits. It also is produced from other titanium minerals or prepared in the laboratory. Pigment-grade dioxide is produced from the minerals, rutile and ilmenite. Rutile is converted to pigment grade rutile by chlorination to give titanium tetrachloride, TiCl4. Anhydrous tetrachloride is converted back to purified rutile form by vapor phase oxidation.
Anatase form is obtained by hydrolytic precipitation of titanium(IV) sulfate on heating. The mineral ilmenite is treated with concentrated sulfuric acid. Heating the sulfate solution precipitates hydrous titanium oxide. The precipitate is calcined to expel all water.
Titanium dioxide also can be prepared by heating Ti metal in air or oxygen at elevated temperatures.
| 調製方法 | Titanium dioxide occurs naturally as the minerals rutile (tetragonal
structure), anatase (tetragonal structure), and brookite (orthorhombic
structure).
Titanium dioxide may be prepared commercially by either the
sulfate or chloride process. In the sulfate process a titanium
containing ore, such as ilemenite, is digested in sulfuric acid. This
step is followed by dissolving the sulfates in water, then precipitating
the hydrous titanium dioxide using hydrolysis. Finally, the
product is calcinated at high temperature. In the chloride process,
the dry ore is chlorinated at high temperature to form titanium
tetrachloride, which is subsequently oxidized to form titanium
dioxide. | 調製方法 | There are two major processes for the manufacture of titanium dioxide
pigments, namely sulfate route and chloride route. In the sulfate
process, the ore limonite, FeOTiO2, is dissolved in sulfuric acid and
the resultant solution is hydrolyzed by boiling to produce a hydrated
oxide, while the iron remains in solution. The precipitated titanium
hydrate is washed and leached free of soluble impurities. Controlled calcinations
at about 1000°C produce pigmentary titanium dioxide of the
correct crystal size distribution; this material is then subjected to a finishing
coating treatment and milling.
The chloride process uses gaseous chlorination of mineral rutile, followed
by distillation and finally a vapor phase oxidation of the titanium
tetrachloride. | 定義 | ChEBI: Titanium dioxide is a titanium oxide with the formula TiO2. A naturally occurring oxide sourced from ilmenite, rutile and anatase, it has a wide range of applications. It has a role as a food colouring. | Composition | This material is visually a brilliant white pigment which also has anti-inflammatory properties. Two crystal types of TiO2 occur: anatase and rutile. In order to produce these crystals, there are two manufacturing processes that are employed: (1) The sulfate manufacturing process has the ability to produce either type of crystal, while (2) the chloride manufacturing process produces only rutile crystals. | 一般的な説明 | Two main physico-chemically distinct polymorphs of TiO2 are anatase and rutile. Anatase has a higher photocatalytic activity than rutile but is thermodynamically less stable. | 危険性 | Lower respiratory tract irritant. Possible
carcinogen. | 健康ハザード | Titanium dioxide is a mild pulmonary
irritant and is generally regarded as a
nuisance dust. | 燃焼性と爆発性 | Notclassified | 応用例(製薬) | Titanium dioxide is widely used in confectionery, cosmetics, and
foods, in the plastics industry, and in topical and oral pharmaceutical
formulations as a white pigment.
Owing to its high refractive index, titanium dioxide has lightscattering
properties that may be exploited in its use as a white
pigment and opacifier. The range of light that is scattered can be
altered by varying the particle size of the titanium dioxide powder.
For example, titanium dioxide with an average particle size of
230nm scatters visible light, while titanium dioxide with an average particle size of 60nm scatters ultraviolet light and reflects visible
light.
In pharmaceutical formulations, titanium dioxide is used as a
white pigment in film-coating suspensions, sugar-coated tablets,
and gelatin capsules. Titanium dioxide may also be admixed with
other pigments.
Titanium dioxide is also used in dermatological preparations
and cosmetics, such as sunscreens. | 安全性プロファイル | A nuisance dust. A
human skin irritant. Questionable
carcinogen with experimental carcinogenic,
neoplastigenic, and tumorigenic data.
Violent or incandescent reaction with metals
at high temperatures (e.g., aluminum,
calcium, magnesium, potassium, sodium,
zinc, lithium). See also TITANIUM
COMPOUNDS. | 安全性 | Titanium dioxide is widely used in foods and oral and topical
pharmaceutical formulations. It is generally regarded as an
essentially nonirritant and nontoxic excipient. | 職業ばく露 | Titanium dioxide is a white pigment used as a pigment in paint; in the rubber, plastics, ceramics, paint, and varnish industries, in dermatological preparations; and is used as a starting material for other titanium compounds; as a gem; in curing concrete; and in coatings for welding rods. It is also used in paper and cardboard manufacture. | 発がん性 | Carcinogenesis. In a 1985 study, rats (CD) were
exposed to graded airborne concentrations (0, 10, 50, and
250mg/m3) of TiO2 6 h/day, 5 days/week, for 2 years. The
majority of the particles were in the respirable range (84%
≤13 mmMMD). All responses were confined to the lungs. At
the lowest dose, the histopathological evaluation of the lungs
revealed dust-laden macrophages in the alveolar ducts and
adjacent alveoli with pneumocyte hyperplasia. At the two
highest concentrations, there were increases in lung weight,
accumulation of dust in the macrophages, foamy macrophage
responses, type II pneumocyte hyperplasia, alveolar proteinosis,
alveolar bronchiolization, cholesterol granulomas, focal
pleurisy, and dust deposition in the tracheobronchiolar lymph
nodes. At the 250mg/m3 exposure concentration, bronchiole
alveolar adenomas (males: control 2/79, 250mg/m3 12/79;
females: control 0/79, 250mg/m3 13/79) increased.
Additionally, 13/79 females at the 250mg/m3 dose showed squamous cell carcinoma, compared with none in 79 controls.
Theauthorsnoted that this responsemight have little biological
relevance to humans because of the overload of respiratory
clearance mechanisms and also pointed out that the type,
location, and development of the tumors were different from
those in human lung tumors. It is not clear that the nasal
cavity epithelium was examined. However, the nasal cavity
load would be expected to be higher in the rats because of
anatomic structure, whereas the lung deposition should be
higher in humans because we are, in part, mouth breathers. | 貯蔵 | Titanium dioxide is extremely stable at high temperatures. This is
due to the strong bond between the tetravalent titanium ion and the
bivalent oxygen ions. However, titanium dioxide can lose small,
unweighable amounts of oxygen by interaction with radiant energy.
This oxygen can easily recombine again as a part of a reversible
photochemical reaction, particularly if there is no oxidizable
material available. These small oxygen losses are important because
they can cause significant changes in the optical and electrical
properties of the pigment.
Titanium dioxide should be stored in a well-closed container,
protected from light, in a cool, dry place. | Structure and conformation | Rutile and anastase crystals are tetragonal. Rutile crystals have greater coverage due to the close packing orientation of the atoms in the crystal. The refractive indices for anatase and rutile crystals are 2.55 and 2.71, respectively. The resultant opacity is due to the light scattering ability of the TiO2. Light, heat, and chemical stability are excellent when employing this material. Additionally, in the United States, TiO2 is regarded as a Category I sunscreen. | 不和合性 | Owing to a photocatalytic effect, titanium dioxide may interact
with certain active substances, e.g. famotidine. Studies have shown that titanium dioxide monatonically degrades film mechanical
properties and increases water vapor permeability of polyvinyl
alcohol coatings when used as an inert filler and whitener.
Titanium dioxide has also been shown to induce photooxidation
of unsaturated lipids. | 不和合性 | Titanium dioxide is incompatible with strong oxidizers and strong acids. Violent or incandescent reactions may occur with metals (e.g., aluminum, calcium, magnesium, potassium, sodium, zinc, and lithium). | 廃棄物の処理 | Land fill. | 規制状況(Regulatory Status) | Accepted as a food additive in Europe. Included in the FDA Inactive
Ingredients Database (dental paste; intrauterine suppositories; ophthalmic preparations; oral capsules, suspensions, tablets; topical
and transdermal preparations). Included in nonparenteral medicines
licensed in the UK. Included in the Canadian List of
Acceptable Non-medicinal Ingredients. |
|